620Mpa Hand Electrode For High Amandla Steel
Isicelo&Standard&Note
1. Ifanele UKUSHISELELWA KWE-CARBON STEEL KANYE NEYAYISHIYA ELIPHANSI, NJENGO-15MnVN.
2. Izinga esihlangabezane nalo: GB/T32533 E5915-3M2 P, AWS A5.5 E9015-D1 & A5.1M E6215-D1, ISO18275-A:E 55 5 Mn1NiMo B 4 2, ISO 18275-B-3 E6215
Lapho ingxenye enkulu ye-carbon ku-high carbon steel ingaphezu kuka-0.60%, ukuqina kwe-post-welding, ukuthambekela kokuzwela kwe-crack kukhulu, ngakho ukushisela kubi kakhulu, akukwazi ukusetshenziselwa ukwakha isakhiwo sokushisela.Ivame ukusetshenziselwa ukwenza izingxenye nezingxenye ezidinga ubulukhuni obuningi noma ukumelana nokugqoka, futhi umsebenzi wayo wokushisela ngokuyinhloko ulungisa ukushisela.
Amaphuzu okunakwa:
1. Ngaphambi kokushisela, i-electrode kufanele ibhakwe ku-350 ℃ ihora elingu-1 futhi ithathwe njengoba kudingeka.
2. Ngaphambi kokushisela, i-weldment kufanele ihlanzwe ngokugqwala, amafutha, amanzi nokunye ukungcola.
3. I-Welding kufanele yenziwe nge-arc emfushane, i-welding pass welding ifanelekile.
Izici
1. I-electrode ye-hydrogen potassium ephansi, i-arc ezinzile, ukwakheka okuhle, okubabazekayo, ukuchaphaza okuncane, i-de-slagging elula, ukumelana nomlilo wesikhumba okuhle, ukumelana okuhle kwe-porosity.
2. Izakhiwo ezizinzile zemishini, ipulasitiki enhle.
Izimpawu nokusetshenziswa: I-sodium hydrogen ephansi yohlobo olunama-electrode ensimbi enamandla amakhulu, isebenzisa i-DC reverse connection, ingaqhuba yonke indawo yokushisela.Ifanele ukushisela i-medium carbon steel kanye nesakhiwo sensimbi esine-alloy ephansi kanye nebanga elihambisanayo lomkhumbi we-pressure kanye ne-pressure pipe welding.Njenge-Q420 (15MnVN) nokunye.Isisekelo sensimbi esishiselayo: Insimbi eshisayo egoqiwe ejwayele ukwenza i-normalizing Q420A (15MnVN, 15MnVNCu, 14MnVTiRE)
Inkampani Nemboni
Ukwakhiwa komkhiqizo kanye nezakhiwo zemishini isingeniso
COMPONET YECHEMICAL:
I-ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S |
GB/T IMITHETHO | 0.12 | 1.00-1.75 | 0.6 | - | 0.9 | 0.25-0.45 | 0.03 | 0.03 |
AWS IMITHETHO | 1.12 | 1.00-1.76 | 1.6 | - | 1.9 | 0.25-0.46 | 0.03 | 0.03 |
ISIBONELO VALUE | 0.078 | 1.58 | 0.36 | 0.04 | 0.73 | 0.37 | 0.011 | 0.007 |
IMPAHLA YOMKHETHI:
IMPAHLA | UKUVUMELA AMANDLA(MPa) | AMANDLA AMANDLA(MPa) | I-HEATTREAMENT℃xh | |||||
GB/T IMITHETHO | 490 | 590 | 620*1 | |||||
AWS IMITHETHO | 530 | 620 | 620*1 | |||||
ISIBONELO VALUE | 553 | 649 | 620*1 |
IMIPHAKATHI YOKUSHISA ENCONYWAYO:
IZINCACISO ZAMA-DIAMETERS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | |||||
Ugesi | H/W | 80-110 | 110-130 | 130-180 | ||||
(Amp) | O/W | 50-80 | 90-120 | 130-160 |
QAPHELA:
H/W: ukushisela indawo enezingqimba
O/W: i-over-head position welding
Amacala Ajwayelekile
Isitifiketi
Ukwakhiwa komkhiqizo kanye nezakhiwo zemishini isingeniso
COMPONET YECHEMICAL:
I-ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S |
GB/T IMITHETHO | 0.12 | 1.00-1.75 | 0.6 | - | 0.9 | 0.25-0.45 | 0.03 | 0.03 |
AWS IMITHETHO | 1.12 | 1.00-1.76 | 1.6 | - | 1.9 | 0.25-0.46 | 0.03 | 0.03 |
ISIBONELO VALUE | 0.078 | 1.58 | 0.36 | 0.04 | 0.73 | 0.37 | 0.011 | 0.007 |
IMPAHLA YOMKHETHI:
IMPAHLA | UKUVUMELA AMANDLA(MPa) | AMANDLA AMANDLA(MPa) | I-HEATTREAMENT℃xh | |||||
GB/T IMITHETHO | 490 | 590 | 620*1 | |||||
AWS IMITHETHO | 530 | 620 | 620*1 | |||||
ISIBONELO VALUE | 553 | 649 | 620*1 |
IMIPHAKATHI YOKUSHISA ENCONYWAYO:
IZINCACISO ZAMA-DIAMETERS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | |||||
Ugesi | H/W | 80-110 | 110-130 | 130-180 | ||||
(Amp) | O/W | 50-80 | 90-120 | 130-160 |
QAPHELA:
H/W: ukushisela indawo enezingqimba
O/W: i-over-head position welding