I-GER-N27L ne-GER-N27 esiyikhiqizayo womabili ama-electrode ensimbi anezinga lokushisa eliphansi le-hydrogen sodium-coated ane-Ni content engu-2.5%, avame ukusetshenziselwa ukushisela izinsimbi ze-ASME SA-203 GrA/B kanye ne-09MnNiDR. Amamodeli e-GER-N27L kanye ne-GER-N27 asebenzisa i-GB/T5117-2012 njengamanje yi-E5015-N5 P/E5015-G P kanye ne-E5515-N5 P ngokulandelana, ahambisana namabanga "I-Welding Materials Product Handbook" eshicilelwe yiMishini. Imboni Press. Ku-W707 kanye ne-W707Ni, izakhiwo ezingokomzimba nezamakhemikhali zensimbi efakiwe zama-electrode amabili ziqhathaniswa kanje.
| Igama | Imodeli | Izingxenye zamakhemikhali% | |||||
| C | Mn | Si | Ni | S | P | ||
| I-GER-N27L | I-E5015-N5P/ I-E5015-GP (W707) | ≤0.05 | ≤1.25 | ≤0.50 | 2.00-2.75 | ≤0.03 | ≤0.03 |
| I-GER-N27 | I-E5515-C1 (W707Ni) | ≤0.12 | ≤1.25 | ≤0.60 | 2.00-2.75 | ≤0.03 | ≤0.03 |
| Igama | Imodeli | Izakhiwo zemishini kanye ne-hydrogen ehlakazekayo | |||||
| I-PWHT | Rm (Mpa) | Rel (Mpa) | A (%) | KV2 (j) | H (mL/100g) | ||
| I-GER-N27L | I-E5015-N5P/ I-E5015-GP (W707) | 605 ±15℃*h | ≥490 | ≥390 | ≥22 | -75℃ I-KV2≥27 | ≤5 |
| I-GER-N27 | I-E5515-C1 (W707Ni) | ≥540 | ≥440 | ≥17 | -60 ℃ I-KV2≥27 | ||
Kungabonakala etafuleni elingenhla ukuthi ukwakheka kwamakhemikhali C kanye no-Si wensimbi efakwe i-GER-N27 (W707Ni) kuphakeme kancane kunaleyo ye-GER-N27L (W707). Ngakho-ke, ngokwamandla, i-GER-N27L (W707) ingeye-electrode yebanga le-490MPa enamandla aphansi. I-GER-N27 (W707Ni) izinga, futhi ukusebenza komthelela kwe-GER-N27L (W707) ehambisanayo kungcono kancane kune-GER-N27 (W707Ni), kodwa ekusebenzeni okungokoqobo, i-GER-N27L (W707) kanye ne-GER-N27 ( W707Ni) umthelela Ukuhlolwa ngokuvamile kwamukelwa ngokuvumelana nenkomba engu -70°C noma -75°C.
① Ngaphambi kokudiliza
② Ngemuva kokususwa kwe-slagging
I-GER-N27L (W707) ukushisela i-fillet eqondile
① Ngaphambi kokudiliza
② Ngemuva kokususwa kwe-slagging
I-GER-N27 (W707Ni) ukushisela i-fillet eqondile
I-GER-N27L ne-GER-N27 zinokushisela okuhle kakhulu kwesikhundla sonke lapho zishisela i-ASME SA-203 GrA/B noma insimbi engu-09MnNiDR (njengoba kukhonjisiwe esithombeni esingenhla sokwakhiwa komthungo wokushisela oqondile wama-electrode amabili), futhi ngokuvamile kunconywa ukuthi amandla omugqa wokushisela akufanele adlule ku-35kJ / cm, ukuze athole isakhiwo esihle kakhulu esibuswa yi-acicular ferrite. Uma i-GER-N27L (W707) isetshenziswa ezintweni ezidinga ukucishwa kanye nokwelashwa kokushisa okubabayo + ukwelashwa kokushisa kwe-annealing, ngokuvamile iwukuthola ukuqina komthelela wezinga lokushisa eliphansi elingcono, kodwa izolahlekelwa amandla athile, futhi amandla aqinile ngokuvamile aphansi 500MPa; I-GER-N27L (W707) Ngaphezu kwemibhoshongo, iphinde isetshenziswe ku-09MnNiDR steel ethylene spherical tanks, kuyilapho i-GER-N27 (W707Ni) ivame ukusetshenziswa ezitsheni ezinokushisa okuphansi ezidinga kuphela ukwelashwa kokushisa kwe-annealing. Okulandelayo kuzonikeza izibonelo zohlelo lokusebenza nokusebenza okuhlobene kwe-GER-N27L ne-GER-N27.
| Izinduku zokushisela | Igama ledivayisi | Ukwelashwa kokushisa kanye nezidingo zobuchwepheshe | Nikeza idatha elinganisiwe |
| I-GER-N27L (E5015-G) | 09MnNiDR umbhoshongo wokumunca igesi | Ukwenza kujwayelekile 915±15℃*1.5h ukupholisa komoya + ukushisa 645±15℃*2.5h ukupholisa komoya+615±15℃*10h Ngemva kokuba isithando somlilo sipholile: I-Rel≥300MPa Rm≥440MPa A%≥23 -70℃KV2≥60J Ubulukhuni HV10≤220 | Rel=347MPa Rm=462MPa A=37% -70℃KV2=255J Ukuqina HV10=151 |
| I-GER-N27L (E5015-N5P) | 09MnNiDR Ithangi eliyindilinga leVinyl | 580±15℃*4h Ngemva kokuba isithando somlilo sipholile: I-Rel≥390MPa Rm≥490MPa A%≥22 -70℃KV2≥54J | Rel=456MPa Rm=538MPa A=27% -70℃KV2=139J |
| I-GER-N27 (E5515-N5P) | 09MnNiDR isitsha se-cryogenic | I-PWHT encane: 590±15℃*3.5h Ngemva kokuba isithando somlilo sipholile: Ubukhulu be-PWHT: PWHT590±15℃*16.5h I-Rel≥440MPa Rm≥540MPa A%≥17 -70℃KV2≥54J | I-PWHT encane: Rel=477MPa Rm=570MPa A=26% -70℃KV2=108J |
| Ubukhulu be-PWHT: Rel=476MPa Rm=566MPa A=28.5% -70℃KV2=112J |
09MnNiDR umbhoshongo wokumunca
09MnNiDR ithangi eliyindilinga le-ethylene